EPS STANDARD GRADE
|
STANDARD GRADE |
SPECIFICATION |
BEADS SIZE MM |
FOAMDENSITY G/L |
USE |
|
301 |
1.00-1.60 |
12.0-14.0 |
GOOD PREEXPANDING |
|
|
302 |
0.85-1.25 |
14.0-16.0 |
||
|
303 |
0.70-1.00 |
15.0-18.0 |
||
|
401 |
0.50-0.80 |
18.0-25.0 |
||
|
501 |
0.40-0.60 |
|
Application
EPS raw material for helmet, surfboards, block，ball
Enlarge:
Item Code:301,302,303,401,501
Features: GOOD ELASTICITY OF FOAM PARTICLES, HIGH EXPANSION RATIO, HIGH STRENGTH OFPRODUCTS,BE ABLE TO EXPAND FOR SEVERAL TIMES; THEY ARE MAINLY APPLICABLE TO PRODUCTION OF LIGHT PLATES.
EPS HIGH EXPANSION GRADE
|
HIGH EXPANSION GRADE |
SPECIFICATION |
BEADS SIZE MM |
FOAMDENSITY G/L |
USE |
|
301 |
1.00-1.60 |
11.0-13.0 |
GOOD ELASTICITY OF FOAM |
|
|
302 |
0.85-1.25 |
13.0-15.0 |
||
|
303 |
0.70-1.00 |
14.0-18.0 |
||
|
401 |
0.50-0.80 |
18.0-20.0 |
||
|
501 |
0.40-0.60 |
20.0-25.0 |
Application
EPS raw material for fish/ice/vegetable box, electric packing
Description:
HIGH EXPANSION GRADE P-301
|
SPECIFICATION |
BEADS SIZE |
FOAM MULTIPLE |
FOAM DENSITY |
EQUAL TO OTHER BRAND |
|
|
LOYAL |
XINDA |
||||
|
P-301 |
1.00-1.60 |
75-90 |
11.0-13.0 |
PMS |
PKF301XJ |
HIGH EXPANSION GRADE P-302
|
SPECIFICATION |
BEADS SIZE |
FOAM MULTIPLE |
FOAM DENSITY |
EQUAL TO OTHER BRAND |
|
|
LOYAL |
XINDA |
||||
|
P-302 |
0.85-1.25 |
65-75 |
13.0-15.0 |
PSA |
PKF302XJ |
HIGH EXPANSION GRADE P-303
|
SPECIFICATION |
BEADS SIZE |
FOAM MULTIPLE |
FOAM DENSITY |
EQUAL TO OTHER BRAND |
|
|
|
|
|
|
LOYAL |
XINDA |
|
PSB |
PKF303XJ |
||||
HIGH EXPANSION GRADE P-401
|
SPECIFICATION |
BEADS SIZE |
FOAM MULTIPLE |
FOAM DENSITY |
EQUAL TO OTHER BRAND |
|
|
LOYAL |
XINDA |
||||
|
P-401 |
0.50-0.80 |
45-55 |
18.0-20.0 |
PS |
PKF401XJ |
HIGH EXPANSION GRADE P-501
|
SPECIFICATION |
BEADS SIZE |
FOAM MULTIPLE |
FOAM DENSITY |
EQUAL TO OTHER BRAND |
|
|
LOYAL |
XINDA |
||||
|
P-501 |
0.40-0.60 |
40-50 |
20.0-25.0 |
P4S |
PKF501XJ |
Item Code:301,302,303,401,501
Features:GOOD FIRE RESISTANT CAPABILITY, HIGH PRE-EXPANSION RATIO AND HIGH STRENGTH OF PRODUCTS; THEY ARE MAINLY APPLICABLE TO THERMAL AND COLD INSULATION MATERIALS OF BUILDINGS.
Description:
|
FIRE |
SPECIFICATION |
BEADS SIZE MM |
FOAMDENSITY G/L |
USE |
|
F-301 |
1.00-1.60 |
70.0-85.0 |
GOOD FIRE RESISTANT CAPABILITY, |
|
|
F-302 |
0.85-1.25 |
60.0-70.0 |
||
|
F-303 |
0.70-0.90 |
50.0-65.0 |
||
|
F-401 |
0.50-0.80 |
40.0-50.0 |
||
|
F-501 |
0.40-0.60 |
30.0-45.0 |
Application
EPS Raw Materials For Polystyrene Cornice,ICF Block,Building Panels,Polystyrene Sandwich Panel, Cement Sandwich panel
Fast Cycling Grade
Specification:
|
Classification |
Spec. |
Diam Range(mm) |
Times |
Density(g/l) |
Use |
|
Fast Cycling Grade |
B-301 |
1.00~1.60 |
55~70 |
14~18 |
Use for electric packing,block and china packing and high density product |
|
B-302 |
0.85~1.25 |
50~60 |
16~20 |
||
|
B-303 |
0.70~0.90 |
40~55 |
18~25 |
||
|
B-401 |
0.50~0.80 |
35~45 |
22~30 |
||
|
B-501 |
0.40~0.60 |
30~40 |
25~35 |
Application
eps raw material for EPS seed tray
Dark Grey EPS
Good fire resistant capability, low thermal conductivity, low energy consumption; they are mainly applicable to higher-level thermal insulation materials of buildings.
Advantages of graphite eps:
1. First class production process worldwide
2. Intelligent DCS
3. Advanced equipments
4. Superior human resorces
5. Quality assurance: ERP and ISO9002
Specifications of graphite eps:
|
Classification |
Spec. |
Diam Range (mm) |
Times |
Density |
Blowing Agent(%) |
Residual SM(ppm) |
Moisture (%) |
Coating |
Oxygen Index(%) |
|
Graphite grade |
HF-301 |
1.00~1.60 |
55~70 |
14~18 |
5.5~6.8 |
≤2000 |
≤2.0% |
≤3200 |
≥30 |
|
HF-302 |
0.85~1.25 |
50~60 |
16~20 |
||||||
|
HF-303 |
0.70~0.90 |
40~55 |
18~25 |
||||||
|
HF-401 |
0.50~0.80 |
35~45 |
22~30 |
||||||
|
HF-501 |
0.40~0.60 |
30~40 |
25~35 |
Applications of graphite eps:
Graphite (SEPS) polystyrene board, called the adiabatic with polystyrene foamed plastic board, graphite mold is a new kind of polystyrene insulation board. Its production process is in polystyrene (EPS) added 5% 50% quality of expanded graphite and 2% - 20% of phosphoric acid compounds as flame retardant, the preparation of expansion by using the method of suspension polymerization PS particles. In polystyrene (EPS) import graphite, make it on the basis of keeping excellent insulation performance, has more excellent flame retardant properties
HIPS 688
Application:
Consumer durables, toys, electronics, housewares, flower pots and growing trays and medical applications
|
Test of Finished Product |
||
|
Item |
Unit Result |
HIPS－688 |
|
Melting flow rate |
g/10min |
5 |
|
Vicat softening point |
℃ |
94 |
|
thermal deformation temperature |
℃ |
－ |
|
tensile strength |
Mpa |
21.5 |
|
extension at break |
％ |
48 |
|
bending strength |
Mpa |
35 |
|
flexural modulus |
Mpa |
－ |
|
cantilever impact strength |
J/m |
98 |
|
Rockwell hardness |
L Scale |
60 |
|
residual styrene content |
mg/kg |
350 |
|
glossiness |
60℃ |
60 |
|
density |
g/cm3 |
1.038 |
HIPS 688E
Application:
Consumer durables, toys, electronics, housewares, flower pots and growing trays and medical applications
|
Test of Finished Product |
||
|
Item |
Unit Result |
HIPS－688E |
|
Melting flow rate |
g/10min |
3.0 |
|
Vicat softening point |
℃ |
93.2 |
|
thermal deformation temperature |
℃ |
83 |
|
tensile strength |
Mpa |
26.0 |
|
extension at break |
％ |
50.0 |
|
bending strength |
Mpa |
61.7 |
|
cantilever impact strength |
J/m |
85.5 |
|
Rockwell hardness |
L Scale |
66 |
|
residual styrene content |
mg/kg |
538 |
|
glossiness |
60℃ |
48.0 |
|
density |
g/cm3 |
1.038 |
GPPS 535
Application:
GPPS has a relatively low cost and is forgiving when processed at high production rates. Extrusion and injection molding
continue to be the predominant processing technologies for PS. Key end use markets for PS include food packaging,
refrigeration, audio/video, consumer electronics and office equipment, medical devices, and toys.
|
Type |
GPS-535 |
|
Melting flow rate |
3.2 |
|
Vicat softening point |
100 |
|
thermal deformation temperature |
80 |
|
tensile strength |
50 |
|
extension at break |
3 |
|
bending strength |
90 |
|
cantilever impact strength |
20 |
|
Rockwell hardness (M scale) |
75 |
|
fog density |
1 |
|
residual styrene content |
below 500 |
|
density |
1.04 |
|
Feature |
middle fluidity, heat resistant |
|
Process |
extrusion |
|
Type of Polymer |
homopolymer |
|
Typical Application |
extruded sheets and foamed |
GPPS525
Application:
GPPS has a relatively low cost and is forgiving when processed at high production rates. Extrusion and injection molding
continue to be the predominant processing technologies for PS. Key end use markets for PS include food packaging,
refrigeration, audio/video, consumer electronics and office equipment, medical devices, and toys.
|
Type |
GPS-525 |
|
Melting flow rate |
7.3 |
|
Vicat softening point |
94 |
|
thermal deformation temperature |
78 |
|
tensile strength |
46 |
|
extension at break |
3 |
|
bending strength |
82 |
|
cantilever impact strength |
20 |
|
Rockwell hardness (M scale) |
70 |
|
fog density |
0.8 |
|
residual styrene content |
below500 |
|
density |
1.04 |
|
Feature |
Middle fluidity,high transparency, good combination property |
|
Process |
injection, extrusion |
|
Type of Polymer |
homopolymer |
|
Typical Application |
AV products,medical/lab/household utensils, etc |
| ADD:No.300-11， street 10, Baiyang, Jianggan, Hangzhou city, Zhejiang, China Zip:310018 | |||
| TEL:86-571-86912702 | FAX:86-571-86912702 | TEL:0086-15990067889 | Whatsup:15990067889 |
| Viber:15990067889 | QQ:313201576 | Wechat:15858131688 | Skype:tonyliao51 |
© 2016 HANGZHOU MINGLONG TECHNOLOGY CO.,LTD. All rights reserved. |
|||